This paper presents results of structural, mechanical and tribological tests of thixocasted and heat-treated hypoeutectic Al-Si alloy A356 (EN-Al Si7Mg0.3). The results of tribological tests were analysed and compared with the results of grey cast iron, which was chose as a standard material for cylinder blocks. The pin-on-disc tribometer was used to carry out tribological tests under dry and lubricated sliding conditions at different loads and speeds. The results showed that thixocasted and heat-treated Al-Si alloy under dry sliding conditions, for applied loads interval, could not be satisfactorily used since plastic flow of the material occurs. However, under lubricated sliding conditions tested material showed a low coefficient of friction without any plastic deformation.Streszczenie
Przedstawiono wyniki badań strukturalnych, mechanicznych i tribologicznych stopu hipoeutektycznego Al-Si A356 (EN-AlSi7 Mg0,3). Wyniki testów tribologicznych zostały porównane z rezultatami uzyskanymi dla żeliwa szarego. W testach użyto stanowiska badawczego typu trzpień–tarcza. Badania obejmowały styk smarowany i niesmarowany dla szeregu wartości obciążenia i prędkości. Stwierdzono, że bez smarowania badany stop nie wykazuje pozytywnych własności z powodu występujących odkształceń plastycznych. W styku smarowanym badany stop wykazał niski współczynnik tarcia i brak odkształceń plastycznych.- Tribology Laboratory, Mechanical Engineering Faculty, University of Belgrade, 11120 Belgrade 35, Serbia, avencl@mas.bg.ac.rs
ZEM_3_09_s_015_024.pdf (1.70 Mb)